    Very new myself although I did learn a little goes a long way and the bible size seems to be related to the diameter of the powder rather than the amount heaping (if the makes any sense). I have only tried it in my table top kiln but the amount to time/heat it took to round the glass was too much for the bubbles. Practice a lot.

    #12981
    Katrinka000
    Participant

    Thank you for your response.  I thought the 100/hr was low enough. Perhaps it was the annealing previously as one half slump first. It did not stick to the mold.  Do you firing with body elements would have been better?  I didn’t hea a crack just saw half slumping w/o the othe half!

     