A piece that was a pot melt within a frame and then fired again on another larger base piece came out looking okay .It was slumped into a very shallow plate mold. I checked it over and top looked okay, bottom appears to have 2 running cracks within part of the interior. They do not come to the surface on either side.
Is it possible to save this piece in any way by firing again? If so, what would be the schedule?