Single purpose firings

[Stephen Richard]

In general it is best to do one thing at a time when kiln forming.  In this case you will not need to take the glassline to full fuse temp, but to a tack fuse.  I would do this first and then slump later.  The saying is that speed kils.  Certainly impatience to get to the finished result often results in breaks or cracks in kiln forming.

Stephen Richard

blogs at: http://www.verrier-glass.blogspot.com/ and  http://www.glasstips.blogspot.com/